Refractory mortars

Technical Specifications

Brand

LF-75

 LF-70 LF-60 LF-50 NF-40 NF-38 NF-34 NF-28

Al2O3 %

Fe2O3 %

75 min.

2.5 max.

 70min.

　

 60min.

　

 50min.

　

 40min.

　

 38min.

　

 34min.

　

 28min.

　

Refractoriness ℃

1790 min.

 1770 min. 1770 min. 1750 min. 1790 min. 1790 min. 1790 min. 1790 min.

　

Fireclay and high alumina castable refractories

Technical Specifications

Brand

GL165

 GL-140 GL-135 GL-130 　 　

Al2O3 %

85 min.

 60min. 42min. 30min. 　 　

Bulk Density g/cm3

after firing at 110℃*24h

　

 　 　 　 　 　

Cold Crushing Strength Mpa

after drying at 110℃*24h

　

25min.

　

 20min. 20min. 10min. 　 　

Modulus Of Rupture MPa

after drying at 110℃*24h

 5min. 4min. 3.5min. 3.5min. 　 　

Test temp.*3h,       ℃

(Permanent Linear Change 1%)

1500

 1400 1350 1300 　 　

Max. Service temperature ℃

1650

 1400 1350 1300