Sliding Plate

Technical Specifications

Brand

Alumina- Graphite- Zirconium

SPAGZ-70

Alumina- Graphite

SPAC-75

High Alumina

SPHA-55

Al2O3 %

F.C %

ZrO2 %

70

7

6

≥75

≥7

 

≥55

 

 

Apparent Porosity, %

10

≤15 ≤14

Bulk Density, g/cm3

3.0

≥2.8 ≥2.4

Cold Crushing Strength, Mpa

110

≥70 ≥70

Modulus Of Rupture MPa

at1400 ℃X0.5hr

8

≥10  

Refractoriness Under Load T2

at 0.196 MPa

1700

   

 

Upper & Lower Nozzle

Technical Specifications

Name of Products

Brand

Upper Nozzle

LNAC-70

Lower Nozzle

UNAC-90

Al2O3 %

F. C %

70

3

90

3

Apparent Porosity %

10

10

Bulk Density g/cm3

2.65

3.0

Cold Crushing Strength Mpa

88

78

Refractoriness Under Load T2

at 0.196 MPa

1700

1700

Well Brick for Sliding Gate

Technical Specifications

Magnesia-graphite well bricks:Resin-bonded. Characterization of raw material ; Electro-fused magnesia: MgO content above 97%, Natural flake graphite: C content above 96%

 

WBMC-10

MgO ,%

F, C ,%

80 min.

10 min.

Apparent Porosity ,%

5 max.

Bulk Density ,g/cm3

2.95 min.

Cold Crushing Strength, MPa

45 min.

Modulus Of Rupture, MPa

at1400

8 min.